Binders/Resins
Ketonic Resin
| Acid Value Max. (KOH/gm) |
Appearance | Viscosity in 50% Ethanol at 30°C (+/-1) |
Melting Point | Hydroxyl Value |
Colour Max. (Gardner Scale) |
Application |
|---|---|---|---|---|---|---|
| 1 | Star Bright Granule | 20 Sec | 92-102°C | 1220-2305 | 1-2 |
NC Paints, Printing Inks, Nail Varnishes, Wood Primer, Peninks, Paper Coating |
Polyvinyl butyral Resin
| Acid Value Max. (KOH/gm) |
Appearance | Viscosity in 50% Ethanol at 30°C (+/-1) |
% Non Volatile | Density (Gms/Ltr) | Poly Vinyl Acetal Content (WT%) | Poly Vinyl Acetate Content (WT%) | Poly Vinyl Alcohol Content (WT%) | Application |
|---|---|---|---|---|---|---|---|---|
| 1 | White Powder | 20 Sec | 98+/-2 | 230-270 | 76 to 79 | 1 to 3 | 16 to 20 |
Printing Inks, Ceramics, Wash Primers, Adhesives |
Cnsl Resin
| % Non Volatile at 120°C/1 Нг | Viscosity at 30°C (±10) in 50% | Application | |
|---|---|---|---|
| 70±2 | 110 | Μ.Τ.Ο. | Red Oxide, Primer, Liquid Insulation |
| 70±2 | 110 | Xylene | Quick Drying dark shade Paint, Primer, Liquid Insulation |
Long oil Resin
| General Ingredients |
% Non Volatile at 120°C/1 Hr |
Oil Length (%) |
Acid Value Application Max. (KOH/gm) |
Viscosity at 30°C (±10) in 50% |
Solvent |
Colour Max. (Gardner) |
Application |
|---|---|---|---|---|---|---|---|
| Soya oil, Penta | 99±1 | 65 | 10 | Z1 – Z3 Gardner | - | 6 |
High solids for decorative enamel for interior and exterior applications. |
| DCO, Penta | 99±1 | 65 | 12 | 130 | - | 9 |
Decorative enamel for interior and exterior applications.
High solid resin for good pigment wetting. |
| Fatty Acid Penta Glycerine |
70/60/50 | 58 | 10 | 190 | M.T.O | 4 | Air drying alkyd for synthetic enamels. |
|
Soya, Penta/ Glycerine |
70±2 | 60 | 14 | 190 | M.T.O | 8 |
Non-Yellowing White for First Quality Enamels |
| Soya, Penta | 80±2 | 60 | 14 | 140 | Xylene | 8 |
For Industrial Texture Finished Product,Wrinkle
Finished Paints |
| DCO, Penta | 80±2 | 65 | 14 | 140 | Xylene | 9 |
For Wrinkle Finished Paints Stipple Finished Paints |
| Fatty Acid, Penta/ Glycerine |
70±2 | 56 | 12 | 170 | M.T.O | 8 |
Good color and gloss retention, good drying.
Decorative enamel for interior and exterior applications. |
Medium oil alkyd Resin
| General Ingredients |
% Non Volatile at 120°C/ 1 Hr |
Oil Length (%) |
Acid Value Application Max. (KOH/gm) |
Viscosity at 30°C (±10) in 40% |
Solvent | Colour Max. (Gardner) |
Application |
|---|---|---|---|---|---|---|---|
| Soya oil, Penta | 60±2 | 51 | 13 | 120 | M.T.O. | 8 |
White enamels & Decorative paints, Non yellowing paints |
| Linseed Oil, Penta | 60±2 | 49 | 10 | 120 | M.T.O. | 9 |
Air Drying Alkyd for Synthetic enamels and undercoats paints |
| Soya Oil, Mixed Polyol | 60±2 | 51 | 12 | 120 | M.T.O | 8 |
Air drying general purpose enamels, Primers |
Rosinated Resin
| General Ingredients |
% Non Volatile at 120°C/ 1 Hr |
Oil Length (%) |
Acid Value Application Max. (KOH/gm) |
Viscosity at 30°C (±10) in 40% |
Solvent | Colour Max. (Gardner) |
Application |
|---|---|---|---|---|---|---|---|
| Soya Rosinated | 60% & 70% | 46 | 10 | 130 | M.T.O. | 10 |
Decorative enamels in pastal shades for interior and exterior use |
| Linseed Rosinated | 60% & 70% | 39 | 11 | 130 | M.T.O. | 12 |
Air Drying Synthetic Enamels and undercoats Paints |
| DCO Rosinated | 60% & 70% | 45 | 10 | 130 | M.T.O | 10 |
Industrial Primer, Good quality air drying enamels |
| Fatty Acid Rosinated | 60% & 70% | 40 | 14 | 130 | M.T.O | 9 | Economic air drying paints and Primers |
Hammertone medium alkyd Resin
| General Ingredients |
% Non Volatile at 120°C/ 1 Hr |
Oil Length (%) |
Acid Value Application Max. (KOH/gm) |
Viscosity at 30°C (±10) in 50% |
Solvent | Colour Max. (Gardner) |
Application |
|---|---|---|---|---|---|---|---|
| Soya Oil, Penta, | 70±2 | 46 | 15 | 80 | Xylene | 12 |
Hammer finish paints, Steel furniture enamels, High corrosion resistance |
| Linseed Oil, Penta, | 70±2 | 39 | 14 | 80 | Xylene | 12 |
Hammer finish paints, Steel furniture enamels, High corrosion resistance |
| DCO, Penta | 70±2 | 45 | 14 | 80 | Xylene | 11 |
Hammer finish paints, Steel furniture enamels, High corrosion resistance |
Short oil alkyd Resin
| General Ingredients |
% Non Volatile at 120°C/ 1 Hr |
Oil Length (%) |
Acid Value Application Max. (KOH/gm) |
Viscosity at 30°C (±10) in 50% |
Solvent |
Colour Max. (Gardner) |
Application |
|---|---|---|---|---|---|---|---|
| Coconut Oil, Glycerine | 70±2 | 31 | 12 | 260 | Xylene | 3 |
For industrial stoving enamels, clear and pigmented NC lacquers and PU systems. |
| DCO, Glycerine | 70±2 | 38 | 12 | 180 | Xylene | 3 |
For polymeric plasticizer with nitrocellulose lacquers for air drying acid cured wood finishes |
|
Saturated Fatty Acid, Glycerine |
70±2 | 35 | 12 | 180 | Xylene | 3 |
Non-yellowing stoving finishing offer excellent gloss and durability. |
| Soya Oil, Glycerine | 70±2 | 40 | 12 | 170 | Xylene | 4 |
Excellent gloss, hardness, flexibility and excellent non yellowing properties in baking enamels |
| Lauric Acid, Glycerine |
70±2 | 30 | 12 | 170 | Xylene | 1 |
Clear and pigmented NC lacquer based top coats for furniture and electrical appliances. Two pack PU systems for metal and wood coatings. |
Specialized alkyd Resin
| General Ingredients |
% Non Volatile at 120°C/ 1 Hr |
Oil Length (%) |
Acid Value Application Max. (KOH/gm) |
Viscosity at 30°C (±10) in 50% |
Solvent |
Colour Max. (Gardner) |
Application |
|---|---|---|---|---|---|---|---|
| Fatty Acid, Penta |
70±2 | 28 | 14 |
40 - 60 sec. 40% Xylene |
Xylene | 6 | For Quick Drying Machinery Paints |
| Fatty Acid, Penta |
70±2 | 32 | 14 | 180 | Xylene | 6 |
Fast drying automotive refinishing Industrial paints, |
|
Fatty Acid, Penta |
70±2 | 43 | 14 | 120 | Xylene | 6 |
For industrial Stoving enamels, Two Pack PU based Coating |
|
Fatty Acid, Mixed Polyol |
70±2 | 38 | 12 | 120 | Xylene | 7 |
Air Drying Auto refinishing works, Industrial Enamelsg |
| Fatty Acid, Mixed Polyol |
55/70 | 24 | 12 | 40 - 60 sec. 40% Xylene | Xylene | 6 |
Very fast drying chainstop alkyd resin for auto mobile finishes. Used in industrial scaffolding finishes. |
|
Fatty Acid, Penta |
60/70 | 38 | 12 | 120 | Xylene | 5 |
Fast drying alkyd resin for automobile finishes. Can be used for 2K PU application. |
Modified alkyn Resin
| General Ingredients |
% Non Volatile at 120°C/ 1 Hr |
Oil Length (%) |
Acid Value Application Max. (KOH/gm) |
Viscosity at 30°C (±10) in 50% |
Solvent |
Colour Max. (Gardner) |
Application |
|---|---|---|---|---|---|---|---|
| Urethane Alkyd | 50 | - | 10 | 1-3 Ps | M.T.O | 6 |
1K urethane alkyd resin for wood metal furniture. For primers enamels for industrial plants. |
| Acrylated alkyd resin | 60±2 | - | 2 | 20-30 Ps @ 250C | Xylene | 5 |
Very fast drying alkyd resin very excellent durability. |
| Styrenated Alkyd Resin | 60±2 | 52 | 10 | 100 | Xylene | 5 | Fast Drying Interior Finish |
Rosin modified maleic Resin
| General Ingredients |
% Non Volatile at 120°C/ 1 Hr |
Melting Point ( °C ) | Acid Value Application Max. (KOH/gm) |
Viscosity at 30°C (±10) 50% |
Solvent | Application |
|---|---|---|---|---|---|---|
| Rosin, Penta | 99±1 | 125-130 | 25 | 55 | - |
Very high gloss, Excellent build in air drying industrial finishes |
| Rosin, Penta | 70±2 | 125-130 | 25 | 55 | Xylene |
Very high gloss, Excellent build in air drying industrial finishes |
| Rosin, Glycerine | 70±2 | 125-130 | 25 | 25 | Xylene | For NC Laquers, Sanding sealers |
| Reduce Phinolic | 99±1 | 125-130 | 25 | 25 | - | Printing inks,Quick Drying varnish |
| Reduce Phinolic | 70±2 | 125-130 | 25 | 25 | Xylene | Printing inks,Quick Drying varnish |
Amino Resin
| General Ingredients |
% Non Volatile at 120°C/ 1 Hr |
Colour Max. (Gardner) |
Acid Value Max. (KOH/gm) |
Viscosity Application in PRA |
% Free Formald ehyde |
MTO Solvent Tolerance |
Solvent | Application |
|---|---|---|---|---|---|---|---|---|
| Butylated MF | 60±2 | 1 | 2 | 12-13 | 3 | 1 : 3-6 | N– Butanol |
Highly reactive Butylated type Curing agent for Stoving paint |
| Butylated MF | 60±2 | 1 | 3 | 10-11 | 3 | 1 : 4-6 | N– Butanol |
Baking finishes for motor cars and kitchen appliances |
| Butylated UF | 60±2 | 1 | 3 | 10-11 | 3 | 1 : 2 | N– Butanol |
Cellulose nitrate polishing lacquers, Very quick in acid curing |
| Butylated UF | 65±2 | 1 | 3 | 10-11 | 0.3 | 1 : 2 | N– Butanol |
Cellulose nitrate polishing lacquers, Very quick in acid curing |